Self-Adhesive Waterproof Membrane/ Roofing Waterproof Membrane/Construction Material for Roof
Description
Basic Info
Surface Treatment | Film Coated |
Function | Waterproof |
Color | Black |
Usage | Outdoor |
Length | 10m, 15m, 20m |
Width | 1m |
Application | Wet Applied /Dry Applied |
Transport Package | Roll |
Specification | width: 1m, length: 10m/15m |
Trademark | YOUSUNNY, Yuxiang |
Origin | Xinxiang, Henan, China |
HS Code | 680710000 |
Production Capacity | 300000 Rolls/Year |
Product Description
Product introduction:Yuxiang self-adhesive polymer modified asphalt waterproof membrane (hereinafter referred to as N type) is based on SBS and other synthetic rubber, high-quality road asphalt and tackifier, polyester film (PET), polyester Vinyl film (PE), aluminum foil or silicon-coated isolation film is the upper surface material, and the lower surface is covered with silicon-coated isolation film as an anti-adhesive layer. It is a self-adhesive polymer modified bitumen tireless base waterproofing membrane.
Main Feature:Cold-bonded construction, does not use open flame, does not use adhesives, does not pollute the environment, and is an environmentally friendly product.Excellent bonding performance, it can be constructed on wet base surface to ensure that the lap joint will not crack and the base surface will not be watered.High tensile strength, large elongation, and strong adaptability to base shrinkage and cracking deformation.It has a unique "self-healing" function, which can heal itself when pierced by sharp hard objects.Strong resistance to damage, if damaged, repair is extremely easy.Application scenarios: suitable for waterproofing projects of industrial and civil building roofs, basements, municipal engineering, reservoirs, swimming pools, bridges, subways, and tunnels. It is especially suitable for waterproof projects such as petroleum depots, chemical plants, textile mills, grain depots where open flames are not suitable.
Instructions for use:Construction process: construction preparation → base treatment → brushing supporting base treatment agent → additional layer construction of detail nodes → talk about baseline → large surface self-adhesive coil laying → exhaust compaction → lap edge compaction and sealing → Facade coil end fixing and sealing → inspection and acceptance → protective layer constructionConstruction preparation: including main materials, auxiliary materials, construction base, site conditions, technical solutions, etc.
Base-level treatment: The base-level should meet the specification requirements, be smooth, clean and dry; the yin and yang corners at the junction of flat and vertical surfaces should be made into circular arcs.Brush the base treatment agent: After the base treatment meets the requirements, brush (or spray) the matching base treatment agent on the surface of the base. The brushing (or spraying) of the base treatment agent should be uniform, and the bottom should not be exposed, and the coil can be laid after the surface is dry.Additional layer construction of nodes: add additional layers to node parts in accordance with relevant specifications or design requirements. The additional layer of general parts is full of glue, and the stress concentration parts should be laid empty according to the requirements of relevant specifications. GB23441-2009
No. | BASE | PY | G | ||||
TYRE | |||||||
1 | Soluble content g/m2 | 2mm | / | 1300 | |||
3mm | 2100 | ||||||
4mm | 2900 | ||||||
2 | Impermeabiity | Pressure .Mpa | 0.3 | 0.2 | 0.3 | ||
Keeping time.min | 30 | ||||||
3 | Heat resistance,"C | 90 | 105 | 90 | 105 | ||
no slippering,no flowing ,no dripping | |||||||
4 | Tension,N/50mm 2 | Longitudinal | 450 | 800 | 350 | 500 | |
transverse | 250 | 300 | |||||
5 | Fracture elongation,%≥ | Longitudinal | 30 | 40 | |||
transverse | |||||||
6 | Cold flexibilty,"C | -18 | -25 | -18 | -25 | ||
No crack | |||||||
7 | Tear resistance,N≥ | Longitudinal | 250 | 350 | 250 | 350 | |
transverse | 170 | 200 | |||||
8 | Phytotrons accelerating ageing | Appearance | First lass | ||||
Tension keeping %2 | Longitudinal | no slipping,no flowing ,no dripping | |||||
80 | |||||||
-10 | -20 | -10 | -20 | ||||
Cold flexibility,ºC | No crack |